Nickel-alloy Hastelloy B-3 UNS N10675 sheet plate
Delivery term:The date of payment from buyers deliver within days-
Price:
Negotiable
- minimum:
- Total supply:
-
Delivery term:
The date of payment from buyers deliver within days
-
seat:
Beijing
-
Validity to:
Long-term effective
-
Last update:
2017-12-30 17:54
-
Browse the number:
88
+
Shanghai Bozhong Metal Group Co. Ltd
- Contactaixin:
Contactaixin:
bozhong(Ms.)
- telephone:
-
Area:
Beijing
Address:BUILDING 32#, NO. 518, XINZHUAN ROAD, SONGJIANG, Shanghai, Shanghai, China (201612)
- Website:
+
Model Number: QJJ009
Brand Name: Bozhong
Key Specifications/Special Features:
Introduction:Super alloys contain number of elements in a variety of combinations to achieve the desired resultThey have good creep and oxidation resistanceThey are available in different shapes, can be used at very high temperatures and mechanical stress, also where high surface stability is requiredCobalt-based, nickel-based, iron-based alloys are three types of super alloysAll of these can be used at temperatures above 540°C (1000°F)Hastelloy (r) C22 (r) is nickel-chromium-molybdenum alloyHas high resistance corrosion and metallurgical stability
Not sensitized during heating or welding
Following datasheet gives more details about Hastelloy (r) C22(r)
Chemical composition
Following table shows the chemical composition of Hastelloy (r) C22 (r)
Element content (%)
Chromium, Cr 20-22.5
Molybdenum, Mo12.5-14.5
Tungsten, W2.5-3.5
Cobalt, Co2.5 min
Iron, Fe2-6
Manganese Mn0.5 max
Vanadium, V 0.35 min
Silicon, Si 0.08 max
Phosphorus, P 0.02 max
Sulfur, S 0.02 max
Carbon, C 0.015 max
Nickel, Ni remainder
Physical properties:
Physical properties of Hastelloy (r) C22 (r) are outlined in the following table
Properties metric imperial
Density: 8.69 g/cm, 0.314 lb/in
Melting point: 1399°C, 2550°F
Mechanical properties:
Mechanical properties of Hastelloy (r) C22 (r) are displayed in the following table
Properties metric imperial
Elastic modulus 206MPa, 29878psi
Thermal properties:
Thermal properties of Hastelloy (r) C22 (r) are given in the following table
Properties metric imperial
Thermal conductivity (at 100°C/212°F) 11.1 W/mK6.4 BTU in/hr.ft.°F
Other designations:
Other designations that are equivalent to Hastelloy (r) C22(r) include:
Machinability:
Hastelloy (r) C22(r) can be machined using high-speed steel tooling
Carbide tools are used for milling or turning
Machining operations can be performed using conventional coolants
Forming:
Hastelloy (r) C22(r) can be easily hot or cold formed followed by heat treatment
Welding:
Except submerged arc welding method, Hastelloy (r) C22 (r) can be welded using all other welding methods
Heat treatment:
Hastelloy (r) C22 (r) is heat treated by annealing at 1122°C (2050°F) followed byquenching
Forging:
Hastelloy (r) C22(r) is hot forged at 1149°C (2100°F)
Not sensitized during heating or welding
Following datasheet gives more details about Hastelloy (r) C22(r)
Chemical composition
Following table shows the chemical composition of Hastelloy (r) C22 (r)
Element content (%)
Chromium, Cr 20-22.5
Molybdenum, Mo12.5-14.5
Tungsten, W2.5-3.5
Cobalt, Co2.5 min
Iron, Fe2-6
Manganese Mn0.5 max
Vanadium, V 0.35 min
Silicon, Si 0.08 max
Phosphorus, P 0.02 max
Sulfur, S 0.02 max
Carbon, C 0.015 max
Nickel, Ni remainder
Physical properties:
Physical properties of Hastelloy (r) C22 (r) are outlined in the following table
Properties metric imperial
Density: 8.69 g/cm, 0.314 lb/in
Melting point: 1399°C, 2550°F
Mechanical properties:
Mechanical properties of Hastelloy (r) C22 (r) are displayed in the following table
Properties metric imperial
Elastic modulus 206MPa, 29878psi
Thermal properties:
Thermal properties of Hastelloy (r) C22 (r) are given in the following table
Properties metric imperial
Thermal conductivity (at 100°C/212°F) 11.1 W/mK6.4 BTU in/hr.ft.°F
Other designations:
Other designations that are equivalent to Hastelloy (r) C22(r) include:
- ASTM B366
- ASTM B564
- ASTM B574
- ASTM B575
- ASTM B619
- ASTM B622
- DIN 2.4602
Machinability:
Hastelloy (r) C22(r) can be machined using high-speed steel tooling
Carbide tools are used for milling or turning
Machining operations can be performed using conventional coolants
Forming:
Hastelloy (r) C22(r) can be easily hot or cold formed followed by heat treatment
Welding:
Except submerged arc welding method, Hastelloy (r) C22 (r) can be welded using all other welding methods
Heat treatment:
Hastelloy (r) C22 (r) is heat treated by annealing at 1122°C (2050°F) followed byquenching
Forging:
Hastelloy (r) C22(r) is hot forged at 1149°C (2100°F)
Form | Specifications | Supply form | Others |
Sheet | Thickness: 0.40-4.75mm General width: 1000, 1219, 1500mm |
Whole coil or piece of it | Cold Annealed, surface 2B, 2E |
Plate | Thickness: 4.76-60mm Width: 1500, 2000, 2500mm Length: 3000, 6000, 8000, 8500mm (under 10mm plate can be coiled) |
Whole coil or piece of it | single hot rolling, solid solution annealed state, surface 1D |
Belt | Thickness: 0.10-3.0mm Width: 50-500mm |
Whole coil or specified size | cold annealed, surface 2B, 2E |
Bar and rod | Rolled bar: Φ5-45mm Length: ≤1500mm |
Polished bar (circle, square) | solutionannealing, decaling |
Forged bar: Φ26-245mm Length: ≤4000mm | |||
Weld tube | Outer diameter: Φ4.76-135mm Wall thickness: 0.25-4.00mm Length: ≤35,000mm |
Base on your requirement | use for PHE |
Seamless tube | Outer diameter: Φ3-114mm Wall thickness: 0.2-4.5mm |
Base on your requirement | use for PHE |
Wire | Outer diameter: Φ0.1-13mm | Base on your requirement | Ni and Ni alloy, Ti and Ti alloy |
Forged piece | roundness and square alloy | Base on your requirement | steel, alloy |
Flangs | all kinds of Flangs | Base on your requirement | steel, alloy |
Welding material | Coil wire: Φ0.90mm/1.2/1.6mm | Base on your requirement | Certificate of origin: America, Sweden, Britain, Germany, Austria, Italy, France |
Straight wire: Φ1.2/1.6/2.4/3.2/4.0mm | |||
Welding rod: Φ2.4/3.2/4.0mm | |||
Tube | elbow, three links, four links, different diameter size | Base on your requirement | Ni and Ni alloy, Ti and Ti alloy |
Explosive bonded laminate | Raw sheet thickness: ≥2mm | Base on your requirement | Ni and Ni alloy, Ti and Ti alloy |
Shipping Information:
- FOB Port: Shanghai
- Lead Time: 10 - 15 days
- HTS Code: 7219.21.00 00
- Dimensions per Unit: 243.8 × 121.9 × 0.6 Centimeters
- Weight per Unit: 50 Kilograms
- Units per Export Carton: 50
- Export Carton Dimensions L/W/H: 250 × 122 × 3 Centimeters
- Export Carton Weight: 8 Kilograms
Main Export Markets:
- Asia
- Australasia
- Central/South America
- Eastern Europe
- Mid East/Africa
- North America
- Western Europe